Giant magnetoresistance in La0.7Pb0.3MnO3 thin film

Анотація

Epitaxial thin films of La_0.7Pb_0.3MnO₃ have been grown on (100) LaAlO₃ and (110) SrTiO₃ substrates by dc magnetron sputtering. The magnetic-field and temperature-dependent resistivity of as-deposited and post-annealed films was examined. At H=10kOe the maximum observed magnetoresistance ratio (R₀-R_H)/R₀ was 62%. The bolometric response to 0.94- m low-frequency modulated radiation in the film with the temperature coefficient of resistance dlnR/dT= 14% was studied. The transport properties are described using Zhang`s spin-polaron theory. An unusual approach to stabilizing the film temperature at the point corresponding to the maximum of the magnetoresistance ratio and responsivity is discussed.